Silver Solder Sheet & Handy Flux Jewelry Soldering Soft Medium Hard Flow 15 Dwt

Description

SILVER SHEET SOLDER & HANDY FLUX
3 GRADES OF SOLDER SHEETS
EASY - MEDIUM - HARD   FLOW GRADES
7oz Handy Flux & 15 DWT SOLDER SHEET FORM
-
Silver solder sheets are used in Jewelry making, in repair work such as sizing and mounting, for assembling silver jewelry, rings and components.
Silver solder comes in 3 grades… the grades are the relative temperature flow points between one and the other.
The softer the solder the less content of silver with a lower melting temperature.
Soldering brazing all purpose, low temperature flux Handy
®
Flux is a long lasting white paste type, very durable won’t break down from prolonged heat, an all-purpose flux for use in brazing and soldering Gold, Silver, Brass, Copper and other Non-Ferrous Metals.
Handy Flux is an active fluoride/borate-type flux which is appropriate for all nonferrous metals and begins to melt and dissolve oxides at 600°F, having an effective temperature range from1100° F-1600° F.
Paste formula can be cleaned up with hot water.
Prior to soldering make sure joints and the solder are clean, flux the full surface area to prevent oxidation and allow for good solder flow, and a good brazed joint.
Soldering Note: Clean - Surface & Joint is important and not too much Solder, good even heat over entire joint area. Clean remove oxides and other soldering residues prior to finishing.
Solder is
Cadmium & Indium FREE
JETS Product #
1924-407+
1925-45S-M-H
3 GRADES Sheet Solder
SPECIFICATIONS:
- Soft/EASY Silver Solder S
heet
, has a melting point of 1260
o
F - 682
o
C. with a Silver Content
of 65%
- Medium Flow
Silver Solder Sheet
, has a melting point of 1295
o
F - 702
o
C. with a Silver Content
of 70%
- Hard Silver Solder Sheet
, has a melting point of 1375
o
F - 746
o
C. with a Silver Content
of 75%
Technical Information:
-
Repairs:
Lower temperature solder is recommended for repair work, especially on pieces that may have been reworked and a high temperature solder may cause a problem.
Assembly Work:
In multiple component soldering use the Higher Temperature Solder first, then a medium grade and finally to a soft the lower melting point.
Production:
High temperature solder, the Hard grade should be used, with the higher silver content, better match of color and a stronger bond. Allowing future repairs to be performed with the softer solders.
Sale is for: Handy Flux 7oz bottle and 3 Grades of Solder Sheet
15DWT Total > (5 DWT of each Grade)
Shipping: Via USPS MAIL
NOTE: Visit
JETSTOOLS
our ebay Store, where you can see other grades of Solder along with listings of Alloy Metals, Brass, Copper and Zinc, various gauges of Copper & Brass Wires and a selection of
J
ewelers
E
quipment
T
ools and
S
upplies
.
JETS Inc.
10B 316 CKSP M